fischer ferritscope-菲希爾鐵素體分析儀

 篤摯儀器代理供應(yīng)*鐵素體分析儀，鐵素體測(cè)試儀，奧氏體和雙相鋼不銹鋼鐵素體分析儀

Chemical, energy and processing plants are often subjectto heat, aggressive media and high pressure. Thesecircumstances demand steel with high corrosion and acid resistance that are resilient even at high temperatures.If the ferrite content is too low, then the weldedmaterial is susceptible to hot-cracking, if the ferrite contentis too high, the toughness, ductility as well as thecorrosion resistance of the steel are reduced. For duplexsteel, a ferrite deficit in the area of the weld seam resultsin stress corrosion cracking and reduction in strength.

The FERITSCOPE FMP30 measures the ferrite content in austenitic and duplex steel according to the magnetic induction method. All magnetisable structure sections are measured i. e., in addition to deltaferrite also strain-induced martensite, for example, or other ferritic phases. It is suited for measurements according to the Basler- Standard and according to DIN EN ISO 17655. Areas of application are onsite measurements, e. g. of austenitic platings as well as weld seams in stainless steel pipes, containers, boilers or other products made of austenitic or duplex steel.

奧氏體不銹鋼焊縫中δ鐵素體的存在會(huì)影響焊縫的強(qiáng)韌性、耐腐蝕性及焊接性,工程現(xiàn)場(chǎng)的焊接過程通常借助鐵素體含量測(cè)定儀來控制δ鐵素體的含量。化工設(shè)備和石油加工廠通常要承受高溫、高壓，同時(shí)要耐腐蝕。外部環(huán)境要求所用鋼材即使在高溫下也要有足夠的耐腐蝕和耐酸性能。如果鐵素體含量太低，焊縫受熱后容易產(chǎn)生裂紋；如果鐵素體含量太高，焊縫將喪失韌性和延展性。對(duì)于雙相鋼，如果鐵素體含量太低，焊縫受到張力或發(fā)生振動(dòng)時(shí)容易破裂。 FeritScope FMP30根據(jù)磁感應(yīng)方法測(cè)量奧氏體鋼和雙相鋼中的鐵素體含量。儀器能識(shí)別所有的磁性部件，也就是說，除了delta鐵素體，還能識(shí)別其轉(zhuǎn)化形式馬氏體。儀器符合Basler標(biāo)準(zhǔn)和DIN 32514-1標(biāo)準(zhǔn)，適合于現(xiàn)場(chǎng)檢測(cè)，可以測(cè)量奧氏體覆層、不銹鋼管道、容器和鍋爐焊縫內(nèi)以及奧氏體鋼或雙相鋼制造的其他產(chǎn)品內(nèi)的鐵素體含量

圖為：焊縫中鐵素體含量的測(cè)量

Calibration / Standards

（校準(zhǔn)/校準(zhǔn)片）

1. 可儲(chǔ)存20,000個(gè)測(cè)量數(shù)據(jù).可儲(chǔ)存100個(gè)應(yīng)用程式，可儲(chǔ)存4000個(gè)數(shù)據(jù)組
2. 數(shù)據(jù)組帶日期和時(shí)間標(biāo)志.統(tǒng)計(jì)功能：平均值、標(biāo)準(zhǔn)偏差、小值、大值和范圍
3. 帶高斯曲線的直方圖顯示， 可輸入工藝公差極限并計(jì)算相應(yīng)的工藝能力指標(biāo)Cp和Cpk
1. 連續(xù)測(cè)量模式下，讀數(shù)還可以在上下限之間模擬顯示
2. 矩陣測(cè)量模式下可以進(jìn)行多點(diǎn)測(cè)量，例如：針對(duì)預(yù)先定義的表面排列.平均測(cè)量模式：僅儲(chǔ)存多個(gè)讀數(shù)的平均值
3. 區(qū)域測(cè)量模式：探頭提起后儲(chǔ)存讀數(shù)并取平均值
4. 離奇值控制功能可自動(dòng)過濾錯(cuò)誤測(cè)量值
5. 可以重寫已儲(chǔ)存的錯(cuò)誤讀數(shù)
6. 應(yīng)用程式連接模式：可共享零位和校準(zhǔn)信息
7. 通過可選的PC軟件MP-Name可為應(yīng)用程式命名
8. 通過可選的PC軟件PC-Datex可將數(shù)據(jù)導(dǎo)出到Excel表格內(nèi).通過可選的PC軟件PC-Datacc可將數(shù)據(jù)導(dǎo)出到Access
9. 電池供電或外接充電器（選配件）

背景和應(yīng)用：

化工設(shè)備和石油加工廠通常要承受高溫、高壓，同時(shí)要耐腐蝕。外部環(huán)境要求所用鋼材即使在高溫下也要有足夠的耐腐蝕和耐酸性能。如果鐵素體含量太低，焊縫受熱后容易產(chǎn)生裂紋；如果鐵素體含量太高，焊縫將喪失韌性和延展性。對(duì)于雙相鋼，如果鐵素體含量太低，焊縫受到張力或發(fā)生振動(dòng)時(shí)容易破裂?；瘜W(xué)和石油化工行業(yè)越來越多地使用雙相鋼，例如：圖1和圖2中的鍋爐容器就是用高防腐性能的雙相不銹鋼制造的。如果焊縫處的鐵素體含量過低，受到張力或發(fā)生振動(dòng)時(shí)容易破裂。然而，在焊接雙相鋼時(shí)，由于焊接添加劑或熱處理不當(dāng)，焊縫處的鐵素體含量非常容易超標(biāo)。只有現(xiàn)場(chǎng)檢測(cè)才能確保處理過程不會(huì)改變*佳的鐵素體含量，防止機(jī)械性能或防腐蝕性能的下降。